Chemical Resistance Films

PFL7YS

Density: 0,92 gr/cm³	Kinetic COF: ≤0,25		One side corona treated; other side heat sealable Standard lamination film can be laminated with different adhesive systems (with solvent, solventless, water based, etc.) and foils – films (BOPET, BOPP, BOPA, paper, etc.) High chemical resistance and resistance to leakage PACKAGE TYPES Pillow, sachet, etc. APPLICATIONS Liquids, wet towels

Thickness (µ)		Seal Initiation Temperature* (C˚)		Heat Seal Strength (N/25mm)
20-39		107-113		17-26
40-79		111-119		25-57
80-119		118-126		49-79
120-149		125-130		77-99
150-199		129-137		97-155
*SIT is the point that film has 90% locked seal

PFL8YS

Density: 0,93 gr/cm³	Kinetic COF: ≤0,25		One side corona treated; other side heat sealable Standard lamination film can be laminated with different adhesive systems (with solvent, solventless, water based, etc.) and foils – films (BOPET, BOPP, BOPA, paper, etc.) Higher chemical resistance than PFL7YS and resistance to leakage PACKAGE TYPES Pillow, sachet, etc. APPLICATIONS Liquids, wet towels

Thickness (µ)		Seal Initiation Temperature* (C˚)		Heat Seal Strength (N/25mm)
20-39		109-113		11-19
40-79		111-119		18-35
80-119		117-124		32-47
120-149		122-128		39-52
150-199		126-131		47-58
*SIT is the point that film has 90% locked seal

PFL9YS

Density: 0,92 gr/cm³	Kinetic COF: ≤0,25		One side corona treated; other side heat sealable Lamination film can be laminated with different adhesive systems (with solvent, solventless, water based, etc.) and foils – films (BOPET, BOPP, BOPA, paper, etc.) Higher chemical resistance than PFL8YS and resistance to leakage PACKAGE TYPES Pillow, sachet, HFFS, VFFS, etc. APPLICATIONS Large/small sized particle powders, wet towels

Thickness (µ)		Seal Initiation Temperature* (C˚)		Heat Seal Strength (N/25mm)
20-39		109-113		10-15
40-79		111-119		15-25
80-119		117-124		22-37
120-149		122-128		29-42
150-199		126-131		37-48
*SIT is the point that film has 90% locked seal